Scientific publications
2024PreprintEnglishOpen access
Checking session…
Scientific publications
Patrick Ndouka Ndouka
Patrick Mountapmbeme Kouotou
Stéphane Kenmoe
Jacques Richard Mache
Dick Hartmann Douma
Ralph Gebauer
ChemRxiv
Herein, Mn3O4 spherical particles (SPs) were synthesized by the sol-gel process, followed by thermal annealing at 400 °C. The sample was analyzed by XRD, FTIR, SEM, SBET, XPS, H2-TPR and UV-vis spectroscopy. XRD and FTIR analysis show that Mn3O4 exhibits a tetragonal spinel structure. SEM and SBET analysis display a porous homogeneous surface made of strongly agglomerated spherical-like grains size with an estimated average particle size of ~35 nm, corresponding to a large specific surface area (SBET) of ~81.5 m2/g. XPS analysis indicated that, Mn3O4 were composed of metallic cations (Mn4+, Mn3+, Mn2+) and oxygen species (O2-, OH- and CO32-). The optical energy band gap energy was ~2.55eV. Moreover, Mn3O4 SPs were successfully tested as catalyst with almost 100% conversion of CH4 to CO2 and H2O at a gas hourly space velocity (GHSV) of 72 000 mL3.g-1h-1. The observed performance can be assigned to the cooperated effects of the smallest spherical-like grain size with mesoporous structure as responsible for the larger SBET, and the available surface-active oxygenated species. The cooperative effect of the good reducibility, the higher ratio of active species (OLat/OAds), as well as Density Functional Theory (DFT) calculations suggested that, CH4 total oxidation over the mesoporous Mn3O4 SPs might follow a two-term process in which both Langmuir-Hinshelwood and Mars-van Krevelen mechanisms are cooperatively involved.